Q460 mixturae laminae cum gravi crassitudine
depictio producti
Descriptio:
Q460 humili robore alte admixtum est ferro. Q ferri robur, 460 MPa, mega est VI potentia X;
et Pa- pressio unitatis Paschalis. Q460 significat deformatio plastica ferri tantum fieri cum robur ferri
attingit 460 MPa, hoc est, dimissa vi externa, ferrum non potest nisi formam virium tenere et reverti non potest.
ad pristinam figuram. Haec vis maior est ferro quam vulgari.
Fundamento, quod humilis carbonis aequivalens obtinet, Q460 materiam microalloying convenienter auget. bonum glutino
effectus exiguum carbonis aequipollens ferri requirit, et incrementum microalloying elementorum vim ferri auget
dum etiam carbonis instar ferri. Fortunate, valde parvum additur carbo aequivalens, ut non afficiat
de ferro wedability.
Compositio chemica:
Gradus | Compositio chemica(%) | |||||||||||
C | Mn | Si | P | S | V | Nb | Ti | AI≥ | Cr | Ni | ||
≤ | ≤ | ≤ | ≤ | ≤ | ≤ | ≤ | ≤ | ≤ | ≤ | |||
Q460 | C | 0.2 | 1.8 | 0.6 | 0.03 | 0.03 | 0.2 | 0.11 | 0.2 | 0.015 | 0.3 | 0.8 |
D | 0.03 | 0.025 | ||||||||||
E | 0.025 | 0.02 |
Mechanica Properties:
Gradus | Delivery | Mechanica Properties | |||||||
Vires cede (Crassitas Min Mpa) | Distrahentes fortitudo | elongatio min.%. | |||||||
≤16mm | 16-40mm | 40—63mm | 63-80mm | 80-100mm | 100—150mm | Min Mpa | ≥34J | ||
Q460 C | Nornalization | 460 | 440 | 420 | 400 | 400 | 380 | 550-720 | ≥17% |
Q460 D | Nornalization | ||||||||
Q460 E | Nornalization |
Productio Show:
Plate Related:
productum notitia
Related laminam offerre possumus:
Nomen | Gradus | T(mm) | W(mm) | Longitudo (mm) | Factor | Partus conditio |
Boiler Ferro Plate | Q245R | 4-85 | 1800-25000 | 8000-12000 | Nangang/Shougang /Xinyu | Normal |
Q245R | 8-44 | 2000/2200/ 2500 | 8000-12000 | Xinyu/Nangang | Normalised | |
Continens Ferro Plate | Q345R(R-HIC) | 8-40 | 2000-25000 | 8000-12000 | Wuyang/Xingcheng | Normalised + unum vitium deprehendatur +Lab report |
15CrMoR | 6-80 | 2000-25000 | 1000/12000 | Wuyang/Xiangtan chalybe | Normalised+temperatus+bis vitium deprehensio | |
09MnNiDR | 6-60 | 2000-25000 | 1000/12000 | Wuyang | Normalised + unum vitium deprehendatur | |
SA516Gr70 | 6-80 | 2000-25000 | 8000-12000 | Wuyang | Normalised + unum vitium deprehendatur | |
SA387Cr11C12 | 6-90 | 2000/22000 | 8000-12000 | Wuyang/Xinyu | Normalised+temperatus+A578B |