Kompożizzjoni Kimika:
| Standard | Grad | Kompożizzjoni Kimika（％） | |||||||||||||
| C | Si | Mn | P | S | Cr | Mo | Cu | Ni | V | Al | W | Nb | N | ||
| ASME SA335 | SA335 P11 | 0.05～0.15 | 0.50～1.0 | 0.30～0.60 | ≤0.030 | ≤0.030 | 1.00～1.50 | 0.50～1.00 | |||||||
| SA335 P12 | 0.05～0.15 | ≤0.50 | 0.30～0.61 | ≤0.030 | ≤0.030 | 0.80～1.25 | 0.44～0.65 | ||||||||
| SA335 P22 | 0.05～0.15 | ≤0.50 | 0.30～0.60 | ≤0.030 | ≤0.030 | 1.90～2.60 | 0.87～1.13 | ||||||||
| SA335 P5 | ≤0.15 | ≤0.50 | 0.30～0.60 | ≤0.030 | ≤0.030 | 4.00/6.00 | 0.45/0.65 | ||||||||
| SA335 P91 | 0.08～0.12 | 0.20～0.50 | 0.30～0.60 | ≤0.020 | ≤0.010 | 8.00～9.50 | 0.85～1.05 | ≤0.40 | 0.18～0.25 | ≤0.015 | 0.06～ 0.10 | 0.03～ 0.07 | |||
| SA335 P92 | 0.07～0.13 | ≤0.50 | 0.30～0.60 | ≤0.020 | ≤0.010 | 8.50～9.50 | 0.30～0.60 | 0.30～0.60 | ≤0.40 | 0.15～0.25 | ≤0.015 | 1.50～2.00 | 0.04～ 0.09 | 0.03～ 0.07 | |
Proprjetà Mekkanika:
| Standard | Grad | Proprjetajiet Mekkaniċi | ||
| Qawwa tar-Rendiment | Saħħa tat-tensjoni | Titwil | ||
| ASME SA335 | SA335 P11 | ≥415 | ≥220 | ≥22 |
| SA335 P12 | ≥415 | ≥220 | ≥22 | |
| SA335 P22 | ≥415 | ≥205 | ≥22 | |
| SA335 P5 | ≥415 | ≥205 | ≥22 | |
| SA335 P91 | 585～760 | ≥415 | ≥20 | |
| SA335 P92 | ≥620 | ≥440 | ≥20 | |
Produzzjoni li offrejna:
Isem tal-prodott | Materjal | Standard | Daqs (mm) | Applikazzjoni |
Tubu b'temperatura baxxa | 16MnDG 10MnDG 09DG 09Mn2VDG 06Ni3ModG ASTM A333 | GB/T18984-2003 ASTM A333 | OD: 8-1240 * WT: 1-200 | Applika għal - 45 ℃ ~ 195 ℃ reċipjent bi pressjoni b'temperatura baxxa u pajp ta 'skambjatur tas-sħana b'temperatura baxxa |
Tubu tal-bojler bi pressjoni għolja | 20G ASTMA106B ASTMA210A ST45.8-III | GB5310-1995 ASTM SA106 ASTM SA210 DIN17175-79 | OD: 8-1240 * WT: 1-200 | Adattat għall-manifattura ta 'tubu tal-bojler ta' pressjoni għolja, header, pajp tal-fwar, eċċ |
Tubu tal-qsim tal-pitrolju | 10 20 | GB9948-2006 | OD: 8-630 * WT: 1-60 | Użat fit-tubu tal-forn tar-raffinerija taż-żejt, tubu tal-iskambjatur tas-sħana |
Tubu tal-bojler bi pressjoni medja baxxa | 10# 20# 16Mn,Q345 | GB3087-2008 | OD: 8-1240 * WT: 1-200 | Adattat għall-manifattura ta 'strutturi varji ta' bojler ta 'pressjoni baxxa u medja u bojler tal-lokomottivi |
Struttura ġenerali tat-tubu | 10#,20#,45#,27SiMn ASTM A53A,B 16Mn,Q345 | GB/T8162-2008 GB/T17396-1998 ASTM A53 | OD: 8-1240 * WT: 1-200 | Applika għall-istruttura ġenerali, appoġġ ta 'inġinerija, ipproċessar mekkaniku, eċċ |
Kejsing taż-żejt | J55,K55,N80,L80 C90,C95,P110 | API SPEC 5CT ISO11960 | OD:60-508*WT:4.24-16.13 | Użat għall-estrazzjoni taż-żejt jew tal-gass fil-kisi tal-bjar taż-żejt, użat fil-ħajt tal-ġenb tal-bjar taż-żejt u tal-gass |
Uri tal-Produzzjoni:
Linja ta' Produzzjoni murija:
Is-Servizz tagħna:
RFQ:
Q1: Inti timmanifattura jew Negozjant
A: Aħna kemm manifattura kif ukoll negozjant
Q2: Tista 'toffri kampjun?
A: Kampjun żgħir jista 'jiġi offrut b'xejn, iżda x-xerrej għandu jħallas il-miżata espressa
Q3: Tista 'toffri servizz ta' pproċessar?
A: Nistgħu noffru qtugħ, tħaffir, pittura, trab tal-kisja eċċ...
Q4: X'inhu l-vantaġġ tiegħek fuq l-azzar?
A: Nistgħu nippersonalizzaw l-istruttura ta 'l-azzar biex nixtru t-tpinġijiet jew it-talba.
Q5: Kif dwar is-servizz loġistiku tiegħek?
A: għandna tim loġistiku professjonali li għandu esperjenza rikka dwar it-tbaħħir, jista 'joffri l-linja tal-vapur stabbli u ta' kwalità.